Sem/eds analysis services with MicroVision Laboratories, Inc. 2021? Problem: A client was a manufacturer of beverages, bottled water, and other drinks. They received a customer complaint through one of their distributors, which indicated that a customer had been drinking a bottle of water, and as they neared the bottom of the bottle, found a mysterious white powder floating in the bottom. The customer returned the bottle and complained. The client hoped to identify the powder so they could both satisfy their end customer, as well as identify any potential problems in their manufacturing or bottling process.
Energy Dispersive X-Ray Spectroscopy (EDS): While in a Scanning Electron Microscope (SEM), samples are exposed to high energy electrons in a vacuum, which generates X-rays through secondary electron transitions. Variations in electron configuration specific to each element generate different energy electrons, and thus different signature energy peaks, indicating which elements are present in the sample. Analysis is performed only on areas which are exposed to the electron beam, facilitating precise control of the analyzed area. This means the composition of very small areas or particles in a sample can be taken. Since EDS is performed in the SEM chamber, a quick and easy interrogation of the surface materials as viewed on the SEM is possible. This can be expanded to include the entire sample, please see our Elemental Mapping page. Additionally, relative amount of the elements present can be calculated, generating composition percentages.
How do I submit a sample or a set of samples? To submit a sample or set of samples, please see the page How to Submit Samples. What if I believe my samples are hazardous? We are not equipped to handle or dispose of every kind of hazardous material. Please call us before sending in any potentially hazardous samples. In cases where we are able to analyze your harzardous samples we may not be able to dispose of them and therefore we will return them to you. Find even more info at find more info. ?We partner with companies in all phases of product development and sales, including R&D, manufacturing, QC, advertising and failure analysis. Our laboratory offers a highly-trained and experienced staff utilizing a powerful set of analytical tools (SEM with EDS and backscatter detectors, Bruker X-Flash elemental mapping, X-Ray imaging, Micro-FTIR spectroscopy, Micro-XRF, light microscopy, cross sectioning/precision polishing and microhardness testing).
Scanning electron microscopy with energy dispersive xray spectroscopy (SEM-EDS) was used to identify the particles. The SEM showed an elevated concentration of iron and iron oxide in the impacted areas. The backscatter electron (BSE) image which correlates brightness in the image with atomic density, highlighted the iron particles that were embedded in the tile and the EDS spectrum confirms the PLM Image chemical composition of these higher density particles.
A client responsible for maintaining the facilities in a public school district called with concerns of a possible mold problem. Areas with high foot traffic, especially those where students tracked water in, were showing dark black spots in the floor tiles. Aggressive cleaning and buffing of the floor would remove the problem for a while, but after several few weeks, the problem resurfaced. The facilities management staff was convinced it was mold related, but sending samples, swabs, and air grabs to a mold lab for culturing showed no sign of fungal structures on the tiles. Read a few more info at microvisionlabs.com.